紙漿纖維製造MCC流程機械流程 Pulp fiber manufacturing MCC process mechanical process

Submitted by super

紙漿纖維製造MCC流程機械流程
Pulp fiber manufacturing MCC process mechanical process

天然產品用於原材料 - 來自當地樹種的木材:山毛櫸,楊樹,cerris橡木
Svilocell EAD的主要產品是漂白硬木牛皮紙漿。
2018年4月8日至4月10日(棣品寄出(4月11日(國際快捷)
簡易機械設備克服試驗對於(山毛櫸,楊樹,cerris橡木) 紙漿板樣品結果流程。
Natural Products for Raw Materials - Wood from Native Tree Species: Beech, Poplar, Cerris Oak
The main product of Svilocell EAD is bleached hardwood kraft pulp.
From April 8th to April 10th, 2018 (defective goods sent (April 11th (International Express))
Simple mechanical equipment overcomes the test results for (puddle, poplar, cerris oak) pulp board sample results.
紙漿纖維製造MCC流程機械流程
1. 濕式紙漿纖維(含水50%)外加水4倍。
2. 乾式紙纖維板(含水2%)外加水6倍。
貴公司經實驗兩棣/品種(含量戊聚醣及灰分含量過高) 纖維分支細密。
Pulp fiber manufacturing MCC process mechanical process
1. Wet pulp fibers (50% water) plus 4 times water.
2. Dry paper fiberboard (2% moisture) plus 6 times water.
Your company has been experimenting with two branches/varieties (excessive pentosan and ash content) with fine fiber branches.
第一階段
(濕式紙漿纖維(含水50%)及乾式紙纖維板(含水2%)處理機械設備經高速輪剪切馬達力150HP為紙纖維角塊。
The first stage
(Wet pulp fiber (50% water content) and dry paper fiberboard (2% moisture content) processing equipment High speed wheel shear motor force 150HP is a paper fiber corner block.
第二階段
紙纖維角塊經螺旋輸送機械設備(入加熱槽桶10噸A.B兩桶、加熱反應及分散和高速攪拌剪切濕液膏紙纖維微細25u以下) 。
second stage
The paper fiber corner piece is conveyed by screw conveying machinery and equipment (into the heating tank 10 tons A.B two barrels, heating reaction and dispersion and high-speed stirring shear wet liquid paste paper fiber fine 25u below)
第三階段
槽桶10噸A.B兩桶轉換(加熱反應及分散和高速攪拌剪切濕液膏紙纖維微細25u以下) 2小時剪切濕液膏紙纖維會自然產熱量。(宇宙立式高速攪拌剪切分散馬達550HP機械設備為濕液膏紙纖維微細25u) 。
1. 濕式紙漿纖維(含水50%)外加水4倍 : 槽桶10噸70%等入水量5,250kg及紙纖維角塊1750kg)。
2. 乾式紙纖維板(含水2%)外加水7倍 : 槽桶10噸70%等入水量6,000kg及紙纖維角塊1,000kg)。
3. 經機械設備高速攪拌分散剪切濕液膏為濕液膏紙纖維微細以達25u細度,外加25%清水2,500kg慢速旋轉(沈澱纖維微細以達25u細度1小時) 讓雜質及(含量戊聚醣及灰分含量過高) 流出。
4. 經螺旋輸送及榨壓水份流出機械設備(戊聚醣水) 含水份130%纖維微細以達25u細度,榨乾棵粒20mm。
The third phase
10 tons of tank A.B two barrels conversion (heating reaction and dispersion and high-speed stirring shear wet paper fiber paper fine 25u below) 2 hours wet wet wipe paper fiber will naturally produce heat. (Cosmic vertical high-speed stirring shearing motor 550HP mechanical equipment for the wet liquid paper fiber fine 25u).
1. Wet pulp fiber (50% water content) plus water 4 times: 10 tons of water, 10 tons of water, 5,250 kg of water, and 1750 kg of paper fiber corners.
2. Dry paper fiberboard (2% moisture) plus water 7 times: 10 tons of water, 10 tons of water into the tank 6,000kg and paper fiber corner block 1,000kg).
3. High speed stirring and shearing wet liquid paste by mechanical equipment for wet solution paper fiber fineness up to 25u fineness, plus 25% water 2,500kg slow rotation (precipitated fiber fineness up to 25u fineness for 1 hour) Let impurities and (The content of pentosan and ash content is too high) Outflow.
4. After spiral conveying and pressing, the water flows out of the mechanical equipment (Pentosan water). The moisture content of 130% of the fiber is fine to reach 25u fineness, and the dried grains are pressed to 20mm.
第四階段
1. 經榨壓含水份130%纖維微細以達25u細度,榨乾棵粒20mm,螺旋輸送入機械設備→輸送入訂量噴霧大自然機能水1比200水 : 螺旋輸送榨乾棵粒20mm。
2. 次數1加工(剪切研磨機械設備馬達力350HP加工細度微40~30u) 自備空壓機及冷卻設備空氣壓力10kg至12kg、溫度5度至10度以下訂量控制噴灑微晶纖維含水份70%,經封密振動篩網200目掉下5u以下微晶細纖維。
3. 次數2加工(切剪研磨機械設備馬達力350HP加工細度微20~12u) 自備空壓機及冷卻設備空氣壓力10kg至12kg、溫度5度至10度以下訂量控制噴灑微晶纖維含水份30%,經封密振動篩網200目掉下5u以下微晶細纖維。
4. 次數3加工(切剪研磨機械設備馬達力350HP加工細度微12~8u) 自備空壓機及冷卻設備空氣壓力10kg至12kg、溫度5度至10度以下訂量控制噴灑微晶纖維含水份20%,經封密振動篩網200目掉下5u以下微晶細纖維。
5. 次數4加工(切剪研磨機械設備馬達力350HP細度微5u以下) 自備空壓機及冷卻設備空氣壓力10kg至12kg、溫度5度至10度以下訂量控制噴灑微晶纖維含水份10%,經封密振動篩網200目掉下5u以下微晶細纖維。
6. 熱風收集乾濕微晶乾燥氣散聚合纖維素含水1%以下) 入機械設備存槽桶微晶纖維均可包裝入庫。日產量微晶細纖產品1,000kg 。
以上紙漿纖維全套製造生產設備24小時全自動人機電腦控制生產。
處理紙漿纖維檢測預估條件?
a. 戊聚醣%1上下b.聚合度掃描120~200上下C. 聚合度120~200上下d. 灰分含量MCC可0.002上下f. 亮度%ISO28上下g. 纖維的大小5um以下。
Fourth stage
1. Pressed water containing 130% fineness of fine fibers to 25u fineness, pressing dried grains 20mm, screwed into the mechanical equipment, transported into the order of spray nature function water 1 to 200 water: spiral conveying dried grains 20mm.
2. Number of times 1 processing (cutting and grinding mechanical equipment motor force 350HP processing fineness of micro 40 ~ 30u) Self-provided air compressor and cooling equipment Air pressure 10kg to 12kg, temperature 5 degrees to 10 degrees below the amount of control spray microcrystalline fiber The moisture content was 70%, and the microcrystalline fine fibers of 5u or less were dropped by 200 meshes of the sealing vibration screen.
3. Number of 2 processing (cutting and shearing grinding machine mechanical force 350HP processing fineness of micro 20 ~ 12u) Self-provided air compressor and cooling equipment Air pressure 10kg to 12kg, temperature 5 degrees to 10 degrees below the amount of control spray microcrystalline fiber The moisture content was 30%, and the microcrystalline fine fibers of 5u or less were dropped by 200 meshes of the sealing vibration screen.
4. Number of times 3 processing (cutting and grinding mechanical equipment motor force 350HP processing fineness micro 12~8u) Self-provided air compressor and cooling equipment air pressure 10kg to 12kg, temperature 5 degrees to 10 degrees below the amount of control spray microcrystalline fiber The moisture content was 20%, and the microcrystalline fine fibers of 5u or less were dropped by 200 meshes of the sealing vibration screen.
5. Number of times 4 processing (cutting and shearing mechanical equipment motor force 350HP fineness micro 5u below) Self-compressed air compressor and cooling equipment air pressure 10kg to 12kg, temperature 5 degrees to 10 degrees below the amount of control spray microcrystalline fiber containing water Parts of 10%, through the 200-mesh vibrating screen to drop 5u microcrystalline fine fibers.
6. Hot air collection Dry and wet microcrystalline dried air-dispersed polymer cellulose with water content less than 1%. Into the mechanical equipment storage tank microcrystalline fiber can be packaged into the storage. Daily production of microcrystalline fine fiber products 1,000kg.
The above full set of pulp fiber manufacturing equipment 24 hours automatic man-machine computer control production.
Processing pulp fiber test estimated conditions?
a. Pentosan %1 up and down b. Degree of polymerization scan 120 to 200 up and down C. Degree of polymerization 120 to 200 up and down d. Ash content MCC

重億興業股份有限公司 盧再傳、王崑正 入製

2018年4月12日

Heavy Industry Co., Ltd. Lu Zaichuan and Wang Kunzheng

April 12, 2018

受邀保加利亞SVILOSA升中崋民國國旗
SVILOSA總裁來台灣訪重億
研究試實驗製作MCC微晶纖維素
試製樣品橡木MCC微晶纖維素
試製樣品三種混合木MCC微晶纖維素
試製樣品三種混合木MCC微晶纖維素